TSINGO® by Nanjing Qingqi is a silane-modified polyether resin, a high-molecular-weight liquid polymer with a high molecular weight polyether backbone. Modified with dimethoxy or trimethoxysilane, it forms an elastomer with moisture in the air when a catalyst is added. It’s a vital resin in sealants and adhesives, widely used across industries for its exceptional performance.Characteristics:
· Exceptional Weather Resistance
· Superior Adhesion
· No Substrate Contamination
· Coatable Surface
· Solvent-Free, Low VOC, Eco-Friendly
Grade：117S
Trimethoxyterminated
Light yellow viscous liquid
Viscosity 7000-8000(mPas/25℃)
Components | Mass fraction | Performance (dumbbell strips) | Unit | Result |
117s | 100 | Tack-free time | min | <120 |
plasticizer | 40 | Hardness | shoreA | 40-45 |
Nano Calcium Carbonate | 140 | Tensile strength | MPa | 2 |
Common calcium carbonat | 0 | 100% stretching strength | MPa | 1.1 |
Dehydrating agent | 2 | Elongation | % | 250 |
Coupling agent | 2 |
|
|
|
Catalyzer | 0.2 |
|
|
|
Test formula
This resin has the characteristics of rapid curing, positioning, strength, and dry surface. The recommended dosage of catalyst DBTL is 0.02-0.2%, which can be adjusted according to surface dryness and curing speed.
TSINGO® by Nanjing Qingqi is a silane-modified polyether resin, a high-molecular-weight liquid polymer with a high molecular weight polyether backbone. Modified with dimethoxy or trimethoxysilane, it forms an elastomer with moisture in the air when a catalyst is added. It’s a vital resin in sealants and adhesives, widely used across industries for its exceptional performance.Characteristics:
· Exceptional Weather Resistance
· Superior Adhesion
· No Substrate Contamination
· Coatable Surface
· Solvent-Free, Low VOC, Eco-Friendly
Grade：117S
Trimethoxyterminated
Light yellow viscous liquid
Viscosity 7000-8000(mPas/25℃)
Components | Mass fraction | Performance (dumbbell strips) | Unit | Result |
117s | 100 | Tack-free time | min | <120 |
plasticizer | 40 | Hardness | shoreA | 40-45 |
Nano Calcium Carbonate | 140 | Tensile strength | MPa | 2 |
Common calcium carbonat | 0 | 100% stretching strength | MPa | 1.1 |
Dehydrating agent | 2 | Elongation | % | 250 |
Coupling agent | 2 |
|
|
|
Catalyzer | 0.2 |
|
|
|
Test formula
This resin has the characteristics of rapid curing, positioning, strength, and dry surface. The recommended dosage of catalyst DBTL is 0.02-0.2%, which can be adjusted according to surface dryness and curing speed.
The company focuses on silane modified polyether resins, serving industries such as construction, automotive, and railway transportation, providing products and basic formulation technology.